The reheat-treated microstructures of cast polycrystalline nickel base superalloy IN-738 turbine blades, operated by Electricity Generating Authority of Thailand (EGAT) for long-term services (70,000 hrs.), were investigated by SEM. It was found that microstructure of the exposed specimen after long-term service can be nearly recovered by a re-solution treatment followed by two-step aging treatments. During solution treatment, the coarse carbides and gamma prime precipitates were partially dissolved into the matrix. Then specimens were treated through series of aging resulting in uniformly dispersed precipitation of gamma prime particles, which is more uniform than those in the long-term exposed microstructure. However, it was also found that the higher solution annealing temperature resulted in less volume fraction of gamma prime precipitates and less homogeneous in microstructure than the lower one.

อิทธิพลของภาวะการอบชุบทางความร้อนต่อการศึกษาคืนสภาพของโครงสร้างจุลภาคของใบพัดกังหันก๊าซที่ทำด้วยโลหะผสมพิเศษเบสนิกเกิลเกรด IN-738 ที่ถูกใช้งานมาเป็นระยะเวลานานประมาณ 70,000 ชั่วโมง โดยการไฟฟ้าฝ่ายผลิตแห่งประเทศไทย ได้ถูกศึกษาและตรวจสอบในงานวิจัยชิ้นนี้ ด้วยกล้องจุลทรรศน์อิเลคตรอนแบบส่องกราด จากการศึกาษพบว่าการทำการละลายอีกครั้งหนึ่งนั้นช่วยทำให้อนุภาคของเฟสแกมมาไพร์มที่โตอย่างไม่เป็นระเบียบหลังจากการใช้งานละลายเข้าไปในเนื้อพื้น (Matrix) เป็นส่วนมาก หลังจากนั้นจะนำไปทำการบ่มแข็งทุติยภูมิและ/หรือปฐมภูมิและทุติยภูมิ ซึ่งจะทำให้เฟสแกรมมาไพร์มที่ตกตะกอนออกมาใหม่ในเนื้อพื้นเป็นอนุภาคขนาดเล็กต่างๆ กัน โดยอยู่เป็นระเบียบในโครงสร้างจุลภาคมากขึ้น ซึ่งจะทำให้ได้โครงสร้างที่มีลักษณะใกล้เคียงกับใบพัดกังหันก๊าซที่ผลิตขึ้นใหม่ก่อนการใช้งาน อย่างไรก็ตาม ยังพบด้วยว่า การทำการละลาย ที่อุณหภูมิสูงเกินไปจะทำให้อนุภาคของแกมมาไพร์มที่ตกตะกอนออกมาใหม่มีปริมาณน้อย และมีขนาดเล็กเกินไป เมื่อเปรียบเทียบกับโครงสร้างจุลภาคที่ได้ด้วยการทำการละลายที่อุณหภูมิต่ำกว่า