M-type strontium ferrites, Sr_0.8La_0.2Fe₁₂O₁₉ have been synthesized by conventional ceramic process. The effects of lanthanum addition and sintering temperature on microstructures and magnetic properties of SrFe₁₂O₁₉ and Sr_0.8La_0.2Fe₁₂O₁₉ samples were investigated. Microstructural analysis of the SrFe₁₂O₁₉ and Sr_0.8La_0.2Fe₁₂O₁₉specimens, sintered at different temperatures revealed that average grain sizes of SrFe₁₂O₁₉ ferrites were larger than that of Sr_0.8La_0.2Fe₁₂O₁₉ ferrite and increased with increasing sintering temperature. The X-ray diffraction (XRD) results confirmed the strontium hexagonal ferrite phase of SrFe₁₂O₁₉ and Sr_0.8La_0.2Fe₁₂O₁₉ compounds. A maximum coercivity value of 4850 Oe and maximum saturation magnetization value of 102 emu/g were obtained for the SrFe₁₂O₁₉ ferrite sintered at 1150 °C and for the SrFe₁₂O₁₉ and Sr_0.8La_0.2Fe₁₂O₁₉ ferrites sintered at 1300 °C, respectively. The remanence (Mr) of Sr_0.8La_0.2Fe₁₂O₁₉ sample sintered at 1200 °C possesses the maximum value of 60 emu/g.