| ชื่อเรื่อง | : | Ammonium nitrate induced cracking of a dryer |
| นักวิจัย | : | Clegg, Richard E. , Tomlins, Rex. , Mackay, Michael. |
| คำค้น | : | Ammonium nitrate. , Stress corrosion. , Reproduced with publisher permission. Definitive version available http://www.sciencedirect.com. u http://www.elsevier.com/wps/find/authorsview.authors/rights (viewed 29/8/2011). , Residual stresses. , Drying agents. , Applied research. , 860602 Inorganic Industrial Chemicals. , 091207 Metals and Alloy Materials. , 091507 Risk Engineering (excl. Earthquake Engineering). , Residual stress -- Ammonium nitrate -- Stress corrosion cracking |
| หน่วยงาน | : | Central Queensland University, Australia |
| ผู้ร่วมงาน | : | - |
| ปีพิมพ์ | : | 2554 |
| อ้างอิง | : | http://hdl.cqu.edu.au/10018/59944 |
| ที่มา | : | Clegg, R, Tomlins, R & Mackay, M 2011, 'Ammonium nitrate induced cracking of a dryer', Engineering Failure Analysis, vol. 18, no. 6, pp. 1559-1564, http://dx.doi.org/10.1016/j.engfailanal.2011.05.016 |
| ความเชี่ยวชาญ | : | - |
| ความสัมพันธ์ | : | Engineering failure analysis. Oxford : Elsevier, 2011. Vol. 18, no. 6 (2011), p. 1559-1564 6 pages Refereed 1350-6307 1350-6307 (online) , ACQUIRE [electronic resource] : Central Queensland University Institutional Repository. |
| ขอบเขตของเนื้อหา | : | - |
| บทคัดย่อ/คำอธิบาย | : | After less than 1 year of service, extensive cracking of two ammonium nitrate prill dryers was found. The cracking was found to be ammonium nitrate-induced stress corrosion cracking and the failure was attributed to a lack of post-weld stress relieving of the fabricated structures. It was considered likely that the SCC would occur more slowly once the cracks had progressed beyond the region of high residual stresses and that the design operating stresses in the dryer would be insufficient to cause rapid cracking in the dryers. In order to manage the dryers until new ones could be fabricated, the dryers were operated normally with regular inspections to monitor crack growth and to date, no significant addition crack growth of major cracks was observed. |
| บรรณานุกรม | : |
Clegg, Richard E. , Tomlins, Rex. , Mackay, Michael. . (2554). Ammonium nitrate induced cracking of a dryer.
กรุงเทพมหานคร : Central Queensland University, Australia. Clegg, Richard E. , Tomlins, Rex. , Mackay, Michael. . 2554. "Ammonium nitrate induced cracking of a dryer".
กรุงเทพมหานคร : Central Queensland University, Australia. Clegg, Richard E. , Tomlins, Rex. , Mackay, Michael. . "Ammonium nitrate induced cracking of a dryer."
กรุงเทพมหานคร : Central Queensland University, Australia, 2554. Print. Clegg, Richard E. , Tomlins, Rex. , Mackay, Michael. . Ammonium nitrate induced cracking of a dryer. กรุงเทพมหานคร : Central Queensland University, Australia; 2554.
|
ridm@nrct.go.th ระบบคลังข้อมูลงานวิจัยไทย รายการโปรดที่คุณเลือกไว้