Melt spinning of poly(methyl methacrylate) fibers was studied for its potential use in optics. PMMA fibers were made, using single screw extruder, under different spinning conditions: extruding temperatures, throughputs rates, and draw ratios to investigate their effects on fiber spinnability and optical properties. Experimental results showed that best spinnability was obtained at extruding temperature 270C and throughput rate 8 rpm such that fibers could be spun continuously without breakage. Poor fiber spinning was obtained at low extruding temperature (230C) as fiber breakage occurred quite often. This is thought to be due to higher stress acting on fibers when low temperature was employed. PMMA fibers obtained showed good light transmission, thus, have potential for applications on optics in new areas, including decoration and clothing.

ศึกษาการปั่นหลอมขึ้นรูปเส้นใยพอลิเมทิลเมทาคริเลตเพื่อการนาไปใช้ในงานด้านแสง โดยทาการปั่นหลอมเส้นใยด้วยเครื่องอัดรีดแบบสกรูเดี่ยวภายใต้สภาวะการขึ้นรูปเส้นใยที่ต่างกัน คืออุณหภูมิการปั่นหลอม อัตราการป้อนเนื้อพอลิเมอร์ และอัตราการลดขนาดเส้นใย จากการวิเคราะห์เส้นใยที่ปั่นหลอมได้เพื่อศึกษาผลของสภาวะการขึ้นรูปเส้นใยต่อความสามารถในการปั่นหลอมและสมบัติการส่องผ่านแสงของเส้นใย พบว่าสภาวะที่อุณหภูมิการปั่นหลอมสูง (270C) และอัตราการป้อนที่ต่า (8 รอบต่อนาที) สามารถปั่นหลอมเส้นใยที่ดีและต่อเนื่อง ในขณะที่อุณหภูมิการปั่นหลอมที่ต่ากว่า (230C ) จะปั่นหลอมได้ยากกว่าโดยเฉพาะเมื่อใช้อัตราการป้อนที่ต่าซึ่งพบว่าเส้นใยขาดในระหว่างการม้วนเก็บอาจเป็นผลเนื่องมาจากเกิดความเค้นสูงบนเส้นใยเมื่อปั่นหลอมด้วยอุณหภูมิต่า เส้นใยพอลิเมทิล-เมทาคริเลตให้ค่าการส่องผ่านของแสงที่ดีทาให้มีแนวโน้มที่จะนาไปใช้ประโยชน์ในงานที่ต้องการสมบัติการนาแสงที่ดี เช่นงานตกแต่งภายใน หรือ เสื้อผ้า ได้