Ceramics with formula (1 − x)Pb(Zr_0.52Ti_0.48)O₃–x(Bi_3.25La_0.75)Ti₃O₁₂ (when x = 0,  0.1,  0.3,  0.5,  0.7,  0.9,  1.0) were prepared by a solid-state mixed-oxide method and sintered at 1150 °C for 4 h. All samples had densities at least 95% of theoretical values. Phase analysis using X-ray diffraction indicated the existence of BLT – as well as PZT – based solid solutions with corresponding lattice distortion. Scanning electron micrographs of ceramic surfaces showed a plate-like structure in BLT-rich phase while the typical grain structure was observed for PZT-rich phase. Ferroelectric measurements of these samples showed that addition of small amounts of BLT into PZT increased coercive field and remanent polarization to about 18 kV/cm and 12.5 μC/cm², respectively. Further increasing the amount of BLT in PZT degraded the ferroelectric properties of the ceramics. This behavior was in agreement with their microstructures and dielectric properties.